200 kilos of Selenium metal are put into a stainless steel reactor (Capacity=2000 liters) (twice the amount to be dissolved, in order to provide a maximum area of contact). Then add 300 kilos of water (three times the weight of selenium), then the mix is heated to >85° Celsius. While stirring the mix, nitric acid is added-at a concentration of 51%- at a rate of about 2 liters per minute (total volume=245 liters).

Reaction produces NOx gases which are being extracted and directed to a gas washer where these are washed using an alkali solution.

Nitric acid addition ends in about two hours, but heating and stirring must continue for 60 or more minutes to ensure there is no free nitric acid left.

Seleniuos Acid so prepared is a yellowish solution, having a specific gravity of about 1,31 g/cm3.

The selenious acid solution is filtered and the rest of undissolved

Selenium metal is left in the reactor to be used in the following reaction.

En un reactor de acero inoxidable de 2000 litros de capacidad se colocan 200 kilos de selenio metálico (el doble de la cantidad a ser disuelta, con el fin de asegurar un áreade ataque máxima) y se mezclan con 300 litros de agua ( tres veces el peso del selenio). La mezcla es calentada a > 85°celsius y se le va agregando ácido nítrico ( a una concentración del 51%) a razón de 2 litros por minuto.( volúmen total 245 litros).

La reacción produce gases Nox, los cuales son derivados a un lavador de gases ad-hoc, en donde son lavados con una solución alcalina.

La adición de ácido nítrico termina en aproximadamente 2 horas, pero el calentamiento y la agitación deberán continuar por aproximadamente 60 minutos más, con el fin de asegurar que no quede acido nítrico libre.

El ácido selenioso así preparado tiene una coloración amarillenta, con una densidad aproximada de 1,31 g/cm3.

El ácido selenioso es filtrado y el resto de selenio metálico no disuelto quedará en el reactor para la próxima disolución.